Surface Finish | Polished |
Form | Slab, tile |
Color | Silver |
Thickness | 10-20 mm |
Water Absorption | 0.1-0.6% |
Material | Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Color | Copper |
Form | Slab, tile |
Material | Slate Stone |
Surface Finish | Polished |
Water Absorption | 0.1-0.6% |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slab Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Form | Slabs |
Color | Copper |
Thickness | 20mm to 50mm |
Edge Finish | Machine Cut,Chamfer,Pencil Edge,Half bullnose,Full bullnose,Rebated bullnose |
Material | Slate Stone |
View Complete details
Surface Finish | Polished |
Form | Slab |
Color | Black |
Thickness | 10-20 mm |
Water Absorption | 0.1-0.6% |
Material | Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Color | Green |
Thickness | 10-20 mm |
Water Absorption | 0.1-0.6% |
Material | Natural Slate stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Form | Slab, tile |
Color | Green |
Water Absorption | 0.1-0.6% |
Material | Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Unpolished |
Form | Blocks, Slabs, Tiles |
Thickness | 10-20 mm |
Material | Slate Stone |
Water Absorption | 0.1-0.6% |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Color | Green |
Form | Slab |
Surface Finish | Polished |
Material | Slate Stone |
Water Absorption | 0.1-0.6% |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Form | Slab, tile |
Color | Ocean Green |
Water Absorption | 0.1-0.6% |
Material | Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Color | Silver Grey |
Form | Slab |
Material | Natural Slate Stone |
Surface Finish | Polished |
Water Absorption | 0.1-0.6% |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Form | Slab |
Color | Silver Grey |
Material | Slate Stone |
Water Absorption | 0.1-0.6% |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished,flammed |
Form | Slab |
Color | Silver |
Thickness | 10-20mm |
Material | Sandstone |
Water Absorption | 0.1-0.6% |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Form | Slab, tile |
Water Absorption | 0.1-0.6% |
Material | Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Surface Finish | Polished |
Form | Slab |
Color | Green |
Water Absorption | 0.1-0.6% |
Material | Natural Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Form | Slab, tile |
Surface Finish | Polished |
Water Absorption | 0.1-0.6% |
Color | Black |
Material | Slate Stone |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Form | Slab |
Surface Finish | Unpolished |
Water Absorption | 0.1-0.6% |
Material | Natural Slate Stone |
Color | Pink |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |
View Complete details
Color | Red |
Thickness | 10-20 mm |
Water Absorption | 0.1-0.6% |
Material | Slate Stone |
Finish | Polished |
Hardness | 6 to 7 on Moh's Scale |
Density | 2.6 to 2.8 Kg/cm3 |
Compressive Strength | 140 to 210 N/mm2 |
Modulus of Rupture | 15 to 25 N/mm2 |
Average Wear | Less than 1% |
Porosity | Quite low |
Weather Impact | Resistant |
Slabs Dimensions: | |
Length Range | 60cm to 150cm |
Width Range | 30cm to 60cm |
Thickness Range | 20mm to 50mm |
Silica (SiO2) | 70-75% |
Al2O3 | 10-15% |
CaO+MgO | Less than 0.5% |
FeO + Fe2O3 | 2-4% |
Alkalies | 4-6% |
TiO2 | Less than 0.5% |
Loss On Ignition (LOI) | Less than 0.5% |